Blish, R. C., II and Vreeland, T., Jr. (1968) Twinning and Slip in Zinc by Indentation. Journal of Applied Physics, 39 (1). pp. 2290-2292. ISSN 0021-8979. http://resolver.caltech.edu/CaltechAUTHORS:BLIjap68a
- Published Version
See Usage Policy.
Use this Persistent URL to link to this item: http://resolver.caltech.edu/CaltechAUTHORS:BLIjap68a
Observations of twinning and slip deformation caused by indentation of zinc reveal that extensive slip on the basal and second-order pyramidal systems takes place at loads up to 5 kg. Prismatic punching through 1-cm crystals is observed at indentation loads in excess of about 2.5 kg. It is concluded that the stress at the tip of the twins cannot be obtained by use of an elastic stress analysis.
|Additional Information:||©1968 The American Institute of Physics. Received 5 December 1967. This work was supported by the U.S. Atomic Energy Commission and the California Institute of Technology.|
|Usage Policy:||No commercial reproduction, distribution, display or performance rights in this work are provided.|
|Deposited By:||Archive Administrator|
|Deposited On:||22 Jul 2008 21:57|
|Last Modified:||26 Dec 2012 10:10|
Repository Staff Only: item control page