Wang, Zhen-Gang (1994) Response and instabilities of the lamellar phase of diblock copolymers under uniaxial stress. Journal of Chemical Physics, 100 (3). pp. 2298-2309. ISSN 0021-9606. http://resolver.caltech.edu/CaltechAUTHORS:WANjcp94
- Published Version
See Usage Policy.
Use this Persistent URL to link to this item: http://resolver.caltech.edu/CaltechAUTHORS:WANjcp94
We study the quasistatic behavior of the lamellar phase of diblock copolymers under uniaxial compression and tension along the normal direction of the layers, in both the weak segregation limit (WSL) and the strong segregation limit (SSL). In the SSL, we derive a (nonlinear) continuum free energy description of the system in terms of local displacement of the lamellar layers, and use this free energy to study the mechanical behaviors. While compression induces the usual Hookian elastic response (for strains or stresses that are not too large), tension leads to square-lattice wave undulations in the transverse directions when the strain exceeds a critical value. In the WSL close to the order–disorder transition temperature, compression can ``melt'' the lamellar phase to the isotropic phase; such a melting can take the form of three types of instabilities, a quasithermodynamic instability, a spinodal at controlled strain, and a mechanical instability at controlled stress. It is shown that the third instability always precedes the second one under controlled-stress conditions. For a weakly first-order transition, the quasithermodynamic instability precedes the mechanical instability; but for a (hypothetical) second-order transition, the mechanical instability appears first as the stress is increased. In the case of tension, a transverse square-lattice wave deformation again develops at a critical strain. This deformation can be followed by a subsequent melting of types similar to the compressional case, upon further increase of the stress or strain. In both the SSL and WSL, the modulus undergoes an abrupt decrease when layer undulation develops, to a value 7/15 of that before the onset of undulation. Because the critical strain for the onset of undulation is usually very small, the modulus for tension will appear different from the modulus for compression, the former being 7/15 of the latter. As a result of this decrease in the modulus, melting of the lamellar phase in the WSL will occur at larger strains under tension than under compression.
|Additional Information:||Copyright © 1994 American Institute of Physics. (Received 16 August 1993; accepted 12 October 1993) The author. wishes to thank J.A. Kornfield for a critical reading of the manuscript and helpful comments. This research was supported in part by a Fellowship from The Institute for Advanced Studies, The Hebrew University of Jerusalem, where the work began. Acknowledgment is also made to the Donors of The Petroleum Research Fund, administered by the American Chemical Society, for additional support.|
|Subject Keywords:||COPOLYMERS; LAMELLAE; PHASE STUDIES; COMPRESSION; TENSION; LAYERS; SEGREGATION; NONLINEAR PROBLEMS; FREE ENERGY; MECHANICAL PROPERTIES; STRAINS; SQUARE LATTICES; ORDER−DISORDER TRANSFORMATIONS; ISOTROPY; MELTING; INSTABILITY; THERMODYNAMICS; SPINODAL DECOMPOSITION; EQUILIBRIUM|
|Usage Policy:||No commercial reproduction, distribution, display or performance rights in this work are provided.|
|Deposited By:||Archive Administrator|
|Deposited On:||15 Sep 2007|
|Last Modified:||05 Oct 2015 21:34|
Repository Staff Only: item control page