Structure and aging characteristics of H_2-permselective SiO_2-Vycor membranes

Tsapatsis, Michael and Gavalas, George (1994) Structure and aging characteristics of H_2-permselective SiO_2-Vycor membranes. Journal of Membrane Science, 87 (3). pp. 281-296. ISSN 0376-7388. https://resolver.caltech.edu/CaltechAUTHORS:20151007-090427609

Full text is not posted in this repository. Consult Related URLs below.

Use this Persistent URL to link to this item: https://resolver.caltech.edu/CaltechAUTHORS:20151007-090427609

Abstract

Hydrogen-permselective membranes were prepared by atmospheric pressure chemical vapor deposition (APCVD) of SiO_2 layers in porous Vycor tubes. The deposition was carried out by passing the reactants SiCl_4 and H_2O through the bore of the support tubes at temperatures ranging from 600 to 800°C. The deposit layers were examined by TEM, SEM, and EPMA. When the deposit was confined inside the pores of the Vycor substrate, the membranes were mechanically stable but when it extended substantially outside of the porous matrix the stresses induced by thermal cycling led to crack formation and propagation. Electron microscopy revealed that the SiO_2 deposit density is maximum in a region ≈0.5 μm thick adjacent to the bore surface and gradually declines to zero within a depth of ≈10 μm from the surface. The thin region of maximum deposit density is responsible for permselectivity, for it essentially blocks the permeation of nitrogen and larger molecules while allowing substantial permeation of hydrogen. This region contains ≈10% by volume trapped voids and as a result has relatively high permeability as suggested by the percolation theory. Annealing at high temperatures causes densification of the deposited material as evidenced by increased activation energy for H_2 permeation and correspondingly reduced permeance. The presence of H_2O vapor accelerates the densification process. The densified membranes had a H_2 permeance as high as 0.1 cm^3(STP)/min-atm-cm^2 at 500°C and a H_2/N_2 permeance ratio above 500.


Item Type:Article
Related URLs:
URLURL TypeDescription
http://dx.doi.org/10.1016/0376-7388(94)87034-9DOIArticle
http://www.sciencedirect.com/science/article/pii/0376738894870349PublisherArticle
ORCID:
AuthorORCID
Tsapatsis, Michael0000-0001-5610-3525
Gavalas, George0000-0003-1468-6835
Alternate Title:Structure and aging characteristics of H2-permselective SiO2-Vycor membranes
Additional Information:© 1994 Elsevier. (Received June 29, 1993; accepted in revised form October 9, 1993) The authors acknowledge the funding of this work by the Department of Energy, University Coal Research Program, under grant DE-FG22-92PC92525. Corning Inc. has supplied the porous Vycor glass tubes used as membrane supports.
Funders:
Funding AgencyGrant Number
Department of Energy (DOE)DE-FG22-92PC92525
Subject Keywords:inorganic membranes; gas separation; membrane preparation and structure; electron microscopy; percolation
Issue or Number:3
Record Number:CaltechAUTHORS:20151007-090427609
Persistent URL:https://resolver.caltech.edu/CaltechAUTHORS:20151007-090427609
Official Citation:Michael Tsapatsis, George Gavalas, Structure and aging characteristics of H2-permselective SiO2-Vycor membranes, Journal of Membrane Science, Volume 87, Issue 3, 2 March 1994, Pages 281-296, ISSN 0376-7388, http://dx.doi.org/10.1016/0376-7388(94)87034-9. (http://www.sciencedirect.com/science/article/pii/0376738894870349)
Usage Policy:No commercial reproduction, distribution, display or performance rights in this work are provided.
ID Code:60851
Collection:CaltechAUTHORS
Deposited By: George Porter
Deposited On:13 Oct 2015 21:35
Last Modified:09 Mar 2020 13:19

Repository Staff Only: item control page