Radiation induced color centers and light monitoring for lead tungstate crystals
- Creators
- Qu, Xiangdong
-
Zhang, Liyuan
-
Zhu, Ren-yuan
Abstract
This paper presents result of a study on undoped as well as various doped lead tungstate crystals. Radiation induced color center density was compared to radio luminescence. Light output degradation for crystals under irradiation was measured. Correlations between variations of crystal transmittance and light output were investigated. Monitoring wavelength was determined so that adequate sensitivity and good linearity may be achieved.
Additional Information
© 2000 IEEE. Work supported in part by U.S. Department of Energy Grant No. DE-FG03-92-ER40701. Prof. Z.W. Yin and P. Lecoq provided samples in this report. Dr. Q. Deng measured sample SIC-167 and BTCP-1965 when he was at Caltech. Many interesting discussions with Drs. E Nessi, P. Lecomte, J.Y. Liao, D.Z. Shen, D.S. Yan and Z.W. Yin are acknowledged.Attached Files
Published - 00914439.pdf
Files
00914439.pdf
Files
(615.8 kB)
| Name | Size | Download all |
|---|---|---|
|
md5:709a6dde0cd5de9635851d48aa44596e
|
615.8 kB | Preview Download |
Additional details
- Eprint ID
- 77673
- Resolver ID
- CaltechAUTHORS:20170523-161746729
- Department of Energy (DOE)
- DE-FG03-92-ER40701
- Created
-
2017-05-23Created from EPrint's datestamp field
- Updated
-
2021-11-15Created from EPrint's last_modified field
- Caltech groups
- CMS@Caltech